Dissolution of a mineral trioxide aggregate sealer in endodontic solvents compared to conventional sealers

Abstract

Abstract The aim of this study is to evaluate the solubility of a Mineral Trioxide Aggregate sealer (MTA-Fillapex) compared with five other sealers, calcium hydroxide (Sealapex), resin (Realseal), zinc oxide-eugenol (Tubli-Seal), and two epoxy resins (AH-26 and AH-Plus), in chloroform and eucalyptoil in static and ultrasonic environments. Samples of each sealer were prepared (n = 180) and then divided into 12 groups that were immersed in solvents for 5 and 10 min in static and ultrasonic environments. The mean weight loss was determined, and the values were compared using Student’s t-test, One-way ANOVA, and Tukey’s HSD post-hoc test (p 0.05). In conclusion, MTA-Fillapex was not sufficiently dissolved in either solvent. Ultrasonic activation had limited effectiveness on MTA-Fillapex dissolution, whereas it significantly increased the efficiency of solvents in dissolving a number of endodontic sealers.

Keywords

• Endodontics
• Root Canal Filling Materials
• Solubility
• Solvents