CuOx supported LaCoO3 perovskite for the photoassisted reverse water gas shift reaction at low temperature

Abstract

CuOx/LaCoO3 systems have been studied for the rWGS reaction under thermal assisted photocatalytic conditions within low temperature range of 180–330 ºC. CuOx species deposited from chemical reduction method over LaCoO3 homogeneously covered the perovskite surface. The reduction pretreatment before reaction leads to the partial Co reduction and the complete reduction of Cu. A significant improvement on CO production has been attained upon Cu incorporation. In addition, upon UV–vis irradiation the CO production is also enhanced. Best results have been obtained for 5 wt% Cu. The highest synergistic effect was observed for the lowest temperature, for which catalytic contribution is negligible. Thus, a good compromise is attained at 300 ºC for which a CO production of 5.45 mmol/h·g and 92 % selectivity, showing a good synergistic effect between thermo and thermo-photocatalytic activity.

Keywords

• Photocatalysis
• Reverse Water Gas Shift
• LaCoO3 perovskite
• CO2 valorization