Micro-Milling of Additively Manufactured Al-Si-Mg Aluminum Alloys

Abstract

Additively manufactured aluminum alloy parts attract extensive applications in various felids. To study the machinability of additively manufactured aluminum alloys, micro-milling experiments were conducted on the additively manufactured AlSi7Mg and AlSi10Mg. By comparing the machinability of Al-Si-Mg aluminum alloys with different Si content, the results show that due to the higher hardness of the AlSi10Mg, the cutting forces are higher than the AlSi7Mg by about 11.8% on average. Due to the increased Si content in additively manufactured Al-Si-Mg aluminum alloys, the surface roughness of AlSi10Mg is 26.9% higher than AlSi7Mg on average. The burr morphology of additively manufactured aluminum alloys in micro-milling can be divided into fence shape and branch shape, which are, respectively, formed by the plastic lateral flow and unseparated chips. The up-milling edge exhibits a greater burr width than the down-milling edge. Due to the better plasticity of AlSi7Mg, the burr width of the down-milling edge is 28.1% larger, and the burr width of the up-milling edge is 10.1% larger than the AlSi10Mg. This research can provide a guideline for the post-machining of additively manufactured aluminum alloys.

Keywords

• additively manufactured aluminum alloys
• processability
• burr formation