Effect of Rapid Solidification and Addition of Cu3P on the Mechanical Properties of Hypereutectic Al-Si Alloys

Abstract

The combined processes; rapid solidification, addition of Cu3P compound and heat treatments to improve the mechanical properties of the hypereutectic Al-13Si, Al-20Si and Al-20Si-1.5Fe-0.7Mn alloys (in wt. %) was studied. Optical microscopy and scanning electron microscopy were used to characterize the microstructures. The mechanical properties were evaluated by tensile tests. It was found that the cooling rate (20-50°C/s) used to solidify the alloys plus the addition of Cu3P compound favored the formation of fine primary Si and the transformation of the Al/Si eutectic from acicular to semi-transformed morphology. The spheroidization of the Al/Si eutectic after heat treatment caused an increase in the elongation (%) compared with the as-cast alloys. Al-13Si alloy showed the highest UTS and elongation (%) values, reaching values up to 215 MPa and 9.6%, respectively. On the other hand, the Al-20Si-1.5Fe-0.7Mn alloy showed the lowest UTS (180MPa) and elongation (3.4%) values. The formation of the Fe-intermetallic compounds caused a negative effect on the mechanical properties of the Al-20Si-1.5Fe-0.7Mn alloy.

Keywords

• Aluminum alloys
• Semi-rapid solidification
• Heat treatment
• Microstructure
• Mechanical properties