Enhanced Mechanical Properties of CLAM by Zirconium Alloying and Thermo-Mechanical Processing

Abstract

In this study, we present the effects of 0.004~0.098 wt% Zr and thermo-mechanical processing (TMP) on the microstructure and mechanical properties of the China RAFM steel, CLAM, as a feasibility study for improving mechanical properties. The inclusions in ingots were characterized using optical microscope (OM) and scanning electron microscope (SEM), which could be classified as fine simple particles and large complex particles. The complexity of the alloy’s inclusion composition increases with the increasing Zr concentration. The higher the Zr content, the more complex the composition of inclusions in the alloy. The average diameter of inclusions in 0.004Zr steel was the smallest, which was 0.79 μm and the volume fraction was 0.018%. The highest yield strength, tensile strength, elongation, and impact energy of 0.004Zr alloy at room temperature were 548.3 MPa, 679.4 MPa, 25.7%, and 253.9 J. The structure of the TMPed steels was all tempered martensite. With the increase in tempering temperature, the yield and tensile strength of the experimental steel gradually decreased, while the elongation and impact energy gradually increased. The 0.004ZrD and 0.004ZrH alloys had the best yield strength and impact energy, which were 597.9 and 611.8 MPa and 225.9 and 243.3 J, respectively. In addition, the alloys showed good thermal stability during the aging at 600 °C for 1500 h. It was discovered that TMP is a simple and practical industrial technique that could successfully enhance the mechanical properties of CLAM steel without sacrificing impact toughness.

Keywords

• China low activation martensitic steel
• Zr
• inclusion
• thermo-mechanical processing
• mechanical properties