Synthesis and mechanical properties of nano-Sb2O3/BPS-PP composites

Abstract

In view of the limitation of wide application of polypropylene(PP) with low strength, poor low-temperature brittleness and easy combustion, a kind of PP matrix nanocomposites was designed and prepared. Sb2O3 nanoparticles (nano-Sb2O3) modified by silane coupling agent of KH550 were dispersed into brominated polystyrene(BPS)-PP matrix by ball milling dispersion and melt blending method, respectively. And the nano-Sb2O3/BPS-PP composites samples were obtained by injection molding method. The effects of nano-Sb2O3 particles on mechanical properties of nano-Sb2O3/BPS-PP composites were investigated. The results showed that the surface of nano-Sb2O3 particles was successfully modified by the KH550 and the interfacial adhesion between nano-Sb2O3 and PP matrix was improved. With increasing of the mass fraction of nano-Sb2O3, the tensile strength and impact strength of nano-Sb2O3/BPS-PP composites were improved accompanying by increasing of crystallinity and refining grain of the composites. When the mass fraction of nano-Sb2O3 was 3 wt%, the tensile strength of nano-Sb2O3/BPS-PP composites was 43 MPa, which was 30.3% higher than that of PP. When the mass fraction of nano-Sb2O3 was 2 wt%, the impact strength of the composites was 44.19 kJ·m−2, which was 30.8% higher than that of PP.

Keywords

• polypropylene
• composites
• sb2o3 nanoparticle
• mechanical properties
• crystallinity