Study on Structural Evolution of Synthetic Graphite Derived from Lignite Prepared by High Temperature–High Pressure Method

Abstract

Abundant and cheap lignite is regarded as inferior fuel due to its disadvantages such as low heat and high moisture. In order to realize the high value and clean, non-fuel utilization of lignite, we used lignite as precursor to prepare high-quality synthetic graphite through graphitization treatment using the high temperature–high pressure (HTHP) method, and afterwards characterized the samples by XRD, Raman, FTIR, SEM-EDS, and HRTEM, and systematically analyzed the effect of P-T conditions on the structure evolution of lignite. Our results demonstrated that temperature dominates the graphitization of lignite, and high pressure accelerates the graphitization process of lignite. Under HTHP treatment, the aromatic layer of lignite accelerates directional rearrangement; the ordered domain increases rapidly, and the ductility and stacking degree of the carbon sheets of the lignite sample are greatly enhanced. Compared with the traditional high-temperature graphitization method, the HTHP method greatly reduces the graphitization temperature and shortens the graphitization time. Remarkably, the as-prepared graphite with a graphitization degree of 91.87% superior to graphite fabricated by the conventional high-temperature processing were rapidly prepared from lignite at 6 GPa and 1300 °C in 20 min. This study demonstrates that the HTHP method is a feasible and effective method to realize the green, efficient, and high value utilization of lignite.

Keywords

• lignite
• graphite
• high graphitization
• HTHP method