1,4-Butanediol Selective Dehydration to 3-Butene-1-ol over Ca–Zr–Sn Composite Oxide Catalysts

Abstract

Ca–Zr–Sn composite oxides catalysts for 1,4-butanediol (BDO) selective dehydration to 3-butene-1-ol (BTO) are synthesized by impregnation and co-precipitation in the present work. The results show that Ca–Zr–Sn catalysts prepared from co-precipitation by using NaOH-Na2CO3 mixing alkali solution as precipitant exhibit an excellent catalytic property for BDO dehydration to BTO. For instance, Ca–Zr–Sn oxide with Ca/Zr and Sn/Zr molar ratio of 0.68 and 0.28 calcined at 650 °C gives a BDO conversion and BTO selectivity of about 97% and 82%, respectively, and exhibits no deactivation during 1000 h scale-up experimental testing. X-ray diffraction results indicate that catalytic active centers for BDO dehydration to BTO are from Ca0.15Zr0.85O crystal phase. NH3- and CO2-temperature programmed desorption prove that the surface of obtained catalysts can provide a large amount of acid and base sites simultaneously. FT-IR spectra of pyridine-adsorbed samples show that acid sites on the surface of Ca–Zr–Sn oxide catalyst mainly exist in a state of Lewis acid, which activates terminal -OH groups of BDO molecule through complexing. The activated -OH interacts with β-H activated on base sites O2− anions relative to Ca species, thereby the CH2=CH- bonds are produced through dehydration to form BTO.

Keywords

• selective dehydration
• 1,4-butanediol
• 3-butene-1-ol
• Ca_0.15Zr_0.85O crystal phase