Formation Mechanism and Control of Solidification Cracking in Laser-Welded Joints of Steel/Copper Dissimilar Metals

Abstract

The solidification cracking behavior in laser welds of steel/copper dissimilar metals was systematically investigated. T2 copper and SUS304 stainless steel were used in the study. The results showed that the occurrence of solidification cracking in welds was the synergistic effect of ε phase liquation, inclusions and composition segregation. During the welding process, the liquation of grain boundaries substantially reduced the cohesion between adjacent grains, as well as the resistance for intergranular crack propagation. The composition segregation inside the grains could induce lattice distortion, thus reducing the plastic deformation capacity of the material itself and concurrently increasing the susceptibility to cracks. In addition, an effective solution for inhibiting solidification cracking was proposed by using an oscillating laser, and the inhibition mechanism was further discussed. Laser oscillating welding significantly promoted grain refinement, solute diffusion and the formation of uniformly distributed ε-Cu precipitated phases in welds. It can improve the intergranular bonding, reduce the susceptibility to solidification cracking and increase the resistance to plastic deformation. The tensile strength of joints using laser oscillating welding is 251 MPa, 35.7% more than 185 MPa using laser welding. Meanwhile, the strain of joints using laser oscillating welding is 3.69, a 96% increase compared to 1.88 using laser welding.

Keywords

• solidification cracking
• dissimilar metals
• laser welding
• composition segregation
• inhibition mechanism