Controllable Electrodeposition Adjusts the Electrochromic Properties of Co and Mo Co-Modified WO₃ Films

Abstract

Metal ion modification is considered to be an effective way to construct metal oxides with specific physical and chemical properties. In this paper, we prepare a tungsten oxide (WO3) film co-modified by Co-ion and Mo-ion to serve as the electrochromic material through a one-step electrodeposition method. The effect of electrodeposition time on film thickness, surface morphology and electrochromic properties is systematically studied as well. The results show that, compared with pure WO3 film, the surface morphology of the tungsten oxide film modified by Co-ion and Mo-ion (WO3: Co, Mo) is significantly different. The Co and Mo co-modified film possesses a higher transmission modulation (58.5% at 600 nm) and rapid switching speed (coloring and bleaching time are 2.7 s and 5.6 s, respectively), low impedance value and excellent cycle stability. The performance enhancement is mainly attributed to the coral-like structure of the membrane, which provides a larger specific surface area, more ion adsorption sites and faster ion diffusion. Therefore, this work provides a fast and low-cost method to prepare tungsten oxide electrochromic films co-modified with cobalt and molybdenum ions. At the same time, it also provides an idea to obtain films with different electrochromic properties by adjusting the film thickness.

Keywords

• electrochromic
• metal ion modification
• structure
• WO₃ film