Las escorias de la central térmica GICC ELCOGAS como materia prima para la síntesis de materiales vitrocerámicos Parte 1: Comportamiento en fusión de las escorias GICC y obtención del vidrio original
Abstract
We report here the results of the first phase of investigation on the melting behavior of the IGCC slag, and the use of this slag as raw component to produce glass ceramics. The vitrifying mixture named ECSCP, is composed by 40% of slag, 30% of glass cullet and 30% of precipitated calcium carbonate obtained as a by-product in a sugar refining plant. This mixture was melted at 1450ºC to obtain the ECSCP parent glass, that was then characterized and its crystallization kinetics studied by thermal analysis. The ECSCP glass exhibit a surface mechanism of crystallization, and will be used to produce anorthite/wollastonite glass ceramics in the second part of the investigation.<br><br>Se exponen aquí resultados de la primera parte de investigación sobre el comportamiento en fusión de las escorias de la central térmica GICC ELCOGAS y el proceso seguido para la obtención de un vidrio utilizando estas escorias como materia prima. Se ha diseñado una mezcla vitrificable (ECSCP) compuesta por un 40% de escorias, un 30% de casco de vidrio y un 30% de carbonato cálcico precipitado de azucarera, que permitió obtener por fusión a 1450 ºC un vidrio homogéneo. El vidrio ECSCP ha sido caracterizado y se ha estudiado su cinética de cristalización a través de análisis térmicos que han puesto de manifiesto un mecanismo de cristalización preferente de tipo superficial. En una segunda parte de la investigación se utilizará este vidrio para obtener materiales vitrocerámicos de anortita/wolastonita.