Effects of Reinforcement Ratios and Sintering Temperatures on the Mechanical Properties of Titanium Nitride/Nickel Composites

Abstract

In this study, powder metallurgy was used to fabricate titanium nitride/nickel metal-matrix composites. First, titanium and nickel powders with weight ratios of 20:80, 50:50 and 80:20 were dry mixed for 24 h. After cold isostatic pressing, the green compacts were soaked in a water-based hot forging lubricant and sintered at 850, 950 and 1050 °C for 1.5 h in an air atmosphere. The effects of the amounts of titanium powder and the sintering temperatures on the mechanical properties (hardness, wear resistance and compressive strength) of the composites were investigated. The results indicated that titanium gradually transformed into titanium nitride near the surface after sintering due to the carbothermal reduction reaction; this transformation was observed to significantly increase the hardness. In addition, an oxygen-rich film was observed to form between the titanium nitride particles and the nickel matrix. An optimum sintering temperature of 950 °C provides the composites (titanium–nickel weight ratios of 20:80) the best mechanical properties (wear resistance and compressive strength) among other groups. Furthermore, increasing the titanium content to 80% in the composite increased the hardness; however, the wear resistance and compressive strength decreased.

Keywords

• titanium
• nickel
• composite
• sintering