The Effects of the Large-Scale Factor on the Integrity Parameters of Monolithic Fire-Resistant Glass

Abstract

Glass is widely used for the manufacture of the facades and interior glazing of buildings. Glass structures are subject to high fire safety requirements. Two methods are employed in this work: experimental studies of small-sized and large-sized samples and simulations of heating glass structures. The results showed that large-sized samples of monolithic tempered glass, with dimensions of 4250 × 2000 × 8 mm and 2000 × 3000 × 8, that were inserted in a steel frame, if properly installed, provided fire resistance limits of E30/E45 and E60, respectively, for loss of integrity, which proves the influence of the dimensions of the glass panel on the fire resistance of the facade structure. The small-sized samples of monolithic tempered glass with dimensions of 1000 × 700 × 8 mm provided a fire resistance limit of E60 for loss of integrity. A large-sized sample of monolithic tempered glass measuring 4250 × 2000 × 8 mm and inserted into an aluminum frame provided a fire resistance limit of E60, proving the effect of the frame on the fire resistance of the structure. According to the results of several simulations, a conclusion was formed about the possibility of predicting the fire resistance limits of tempered glass based on its thickness and dimensions. During operations, these structures will be able to prevent the spread of fire and combustion products for the required time after the loss of integrity. The results of the study allow for the estimation of the influence of the scale factor on the falling of the glass from the frame in a fire (loss of integrity).

Keywords

• buildings
• glass structure
• fire resistance
• monolithic fire-resistant glass
• loss of integrity
• cracking