Studies on the mechanical and thermal stability of Calotropis gigantea fibre-reinforced bran nano particulates epoxy composite

Abstract

Abstract In recent trends, the usage of synthetic materials has been reduced by introducing natural fibres for lightweight applications. In this study, Madar (Calotropis gigantea) fibre is selected for the reinforcement phase (40%), and the epoxy polymer is blended with bran filler selected as a matrix material. To calculate hybrid composite mechanical characteristics, five composite laminates with different fibre/filler weight ratios were made. The results show that when the weight ratio of madar fibre increased, the superior mechanical properties were observed in the composite laminate sample (A), such as tensile strength (20.85 MPa), flexural strength (24.14 MPa), impact energy absorption (23 J) compared with an increasing the weight ratio of bran nanofiller to this composite material. At the same time, increasing bran nanofillers can improve thermal stability up to 445 °C of degrading temperature. To analyse the surface interaction between the madar fibres, bran nanofillers, and epoxy matrix by conducting the scanning electron microscope (SEM) analysis before subjecting to the mechanical test and also to identify the failure mode by conducting the SEM test after the laminates are broken during the mechanical tests of the hybrid composite.