Vat Photopolymerization Additive Manufacturing Resins: Analysis and Case Study

Abstract

Abstract Additive manufacturing processes have been developed over the last decades, especially vat photopolymerization (VP) processes, due to its simplicity and speed. The objective of this paper is to characterize commercial VP resins widely used for technical applications. Thus, test specimens were printed by Digital Light Processing and subjected to tensile, compression, flexural, hardness, and inorganic composition analyses. The resin with the highest resistance and hardness (containing 0.6 vol% of inorganics load) reached 53 MPa in tension, 110 MPa in compression, 79 MPa in bending, and 82.3 Shore D, which is comparable to injected polymers. A case study was made, replacing the injected gears of a reducer by printed ones and comparing the finite element analysis with resin properties. The characterization and case study results encourage the expansion of VP processes in the manufacturing of products in several industries and service sectors, as well as the development of new composite resins.

Keywords

• 3D printing
• FEM
• photopolymerization
• DLP