Preparation and flame retardant properties of new mining fireproof gel

Abstract

Coal spontaneous combustion (CSC) brings great danger to mine safety. Although traditional colloidal fire-fighting materials can reside at high fire source points, their permeability and fluidity are poor, and such materials focus on their water absorption, but pay less attention to water retention and resistance, which makes their fire-fighting effect not good. This paper proposed a new type of mining fire prevention colloid material (CPS-α), which had good solid water gel formation, viscosity, fluidity, and blocking properties to compensate for traditional colloids' shortcomings. According to the single-factor experiment, polymeric polyacrylamide (PAM) as the base material, sodium carboxymethyl cellulose (CMC) as the coagulant, modified starch (SS) as the flame retardant and reduced ascorbic acid were determined. After gel treatment, compared with raw coal, the critical temperature point of spontaneous combustion of coal was increased by about 28 °C, the time to reach the critical temperature point was delayed by 190s, and the characteristic temperature points were significantly increased; the overlap area of coal and water increases by about 20 % after adding gel, and the change slope of the diffusion coefficient of water decreases, which indicated that CPS-α had good flame retardant effect.

Keywords

• Spontaneous coal combustion
• Composite flame retardant materials
• Ratio optimization
• Flame retardant properties
• Kinetic analysis