Interfacial Reaction Mechanism between Ceramic Mould and Single Crystal Superalloy for Manufacturing Turbine Blade
Jiansheng Yao,
Longpei Dong,
Zhenqiang Wu,
Lili Wang,
Bin Shen,
Xiaowei Yang
Affiliations
Jiansheng Yao
Science and Technology on Advanced High Temperature Structural Materials Laboratory, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China
Longpei Dong
Science and Technology on Advanced High Temperature Structural Materials Laboratory, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China
Zhenqiang Wu
Science and Technology on Advanced High Temperature Structural Materials Laboratory, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China
Lili Wang
Science and Technology on Advanced High Temperature Structural Materials Laboratory, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China
Bin Shen
Science and Technology on Advanced High Temperature Structural Materials Laboratory, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China
Xiaowei Yang
Science and Technology on Advanced High Temperature Structural Materials Laboratory, AECC Beijing Institute of Aeronautical Materials, Beijing 100095, China
Single crystal superalloys are the preferred materials for manufacturing turbine blades of advanced aero-engines, due to their excellent high temperature comprehensive performance. The interfacial reaction between alloys and ceramic mould are an important factor to influence the surface quality and service performance of the turbine blade. It is very important to reveal the interfacial reaction mechanism to improve turbine blade quality and yield rate. In this paper, the interfacial reactions between DD6 single crystal superalloy and ceramic mould were investigated by scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction analysis (XRD). The results show that the main reaction products were HfO2, Al2O3 and Y3Al5O12 when the yttrium oxide powders were the prime coat materials, while alloy surface suffered undesirable sand fusion; the thicknesses of the reaction layers were over 20 μm. The reaction layer can be divided into two layers, the layer close to the alloy was mainly composed of Al2O3 and Y3Al5O12, and the layer close to the mould was composed of SiO2, Al2O3 and Y3Al5O12. Avoiding the formation of Y2O3-Al2O3-SiO2 ternary low-melts can solve the interfacial reaction between DD6 alloy and yttrium oxide mould.