Boletín de la Sociedad Española de Cerámica y Vidrio (Aug 2005)
Influencia de características microestructurales de caolinita en las propiedades de sus pastas de colaje
Abstract
The granulometrical, chemical, mineralogical and microestructural characterizations of 9 kaolins and 4 clays widely used as raw materials at the Manises ceramic cluster were performed. Technological properties such as viscosity, thickness formation speed, shrinkage, water absorption and apparent density of all materials were studied. The aim of the work is to analyse the relationships between the characteristics of the materials and their technological properties, paying special attention to the kaolinite crystallite size. Significant relationships between kaolinite crystallite size and properties after firing such as water absorption and apparent density were found. The most important characteristic was the clay fraction, showing relationship with water absorption, apparent density and casting rate.<br><br>En el presente trabajo se realiza la caracterización granulométrica, mineralógica, química y microestructural de 9 caolines y 4 arcillas de amplio uso en el clúster cerámico de Manises. Se determinan propiedades en crudo (viscosidad, velocidad de formación de capa) y en cocido (absorción de agua, contracción, densidad aparente) y se analizan las relaciones existentes entre dichas propiedades y las características composicionales, prestándose especial atención a la influencia de la microestructura de la caolinita. Se concluye que existe relación entre el tamaño de cristalito de la caolinita y propiedades en cocido como la absorción de agua y la densidad aparente. Destaca como principal parámetro de composición el contenido en fracción fina de los materiales, que se relaciona con la densidad aparente, la absorción de agua, y la velocidad de formación de pared.