Large-Scale Synthesis of Semiconducting Cu(In,Ga)Se<sub>2</sub> Nanoparticles for Screen Printing Application

  • Bruna F. Gonçalves,
  • Alec P. LaGrow,
  • Sergey Pyrlin,
  • Bryan Owens-Baird,
  • Gabriela Botelho,
  • Luis S. A. Marques,
  • Marta M. D. Ramos,
  • Kirill Kovnir,
  • Senentxu Lanceros-Mendez,
  • Yury V. Kolen’ko

DOI
https://doi.org/10.3390/nano11051148
Journal volume & issue
Vol. 11, no. 5
p. 1148

Abstract

Read online

During the last few decades, the interest over chalcopyrite and related photovoltaics has been growing due the outstanding structural and electrical properties of the thin-film Cu(In,Ga)Se2 photoabsorber. More recently, thin film deposition through solution processing has gained increasing attention from the industry, due to the potential low-cost and high-throughput production. To this end, the elimination of the selenization procedure in the synthesis of Cu(In,Ga)Se2 nanoparticles with following dispersion into ink formulations for printing/coating deposition processes are of high relevance. However, most of the reported syntheses procedures give access to tetragonal chalcopyrite Cu(In,Ga)Se2 nanoparticles, whereas methods to obtain other structures are scarce. Herein, we report a large-scale synthesis of high-quality Cu(In,Ga)Se2 nanoparticles with wurtzite hexagonal structure, with sizes of 10–70 nm, wide absorption in visible to near-infrared regions, and [Cu]/[In + Ga] ≈ 0.8 and [Ga]/[Ga + In] ≈ 0.3 metal ratios. The inclusion of the synthesized NPs into a water-based ink formulation for screen printing deposition results in thin films with homogenous thickness of ≈4.5 µm, paving the way towards environmentally friendly roll-to-roll production of photovoltaic systems.

Keywords