Preparation and Electrochemical Characterization of Si@C Nanoparticles as an Anode Material for Lithium-Ion Batteries via Solvent-Assisted Wet Coating Process

Abstract

Silicon-based electrodes are widely recognized as promising anodes for high-energy-density lithium-ion batteries (LIBs). Silicon is a representative anode material for next-generation LIBs due to its advantages of being an abundant resource and having a high theoretical capacity and a low electrochemical reduction potential. However, its huge volume change during the charge–discharge process and low electrical conductivity can be critical problems in its utilization as a practical anode material. In this study, we solved the problem of the large volume expansion of silicon anodes by using the carbon coating method with a low-cost phenolic resin that can be used to obtain high-performance LIBs. The surrounding carbon layers on the silicon surface were well made from a phenolic resin via a solvent-assisted wet coating process followed by carbonization. Consequently, the electrochemical performance of the carbon-coated silicon anode achieved a high specific capacity (3092 mA h g−1) and excellent capacity retention (~100% capacity retention after 50 cycles and even 64% capacity retention after 100 cycles at 0.05 C). This work provides a simple but effective strategy for the improvement of silicon-based anodes for high-performance LIBs.

Keywords

• silicon anode
• carbon coating
• lithium-ion batteries
• phenolic resin