The Synthesis of Narrowly Dispersed Poly(ε-caprolactone) Microspheres by Dispersion Polymerization Using a Homopolymer Poly(dodecyl acrylate) as the Stabilizer

Abstract

Using dodecyl acrylate as a raw material and 2-Cyanoprop-2-yl-dithiobenzoate as a chain transfer agent, poly(dodecyl acrylate) is synthesized by reversible addition–fragmentation chain transfer (RAFT) polymerization. Using poly(dodecyl acrylate) as stabilizers, narrowly dispersed poly(ε-caprolactone) microspheres with particle sizes ranging from 0.5 to 1.5 μm are successfully synthesized by ring-opening dispersion polymerization. The effects of the molecular weight of poly(dodecyl acrylate), the volume proportion of mixed solvent (i.e., 1,4-dioxane/heptane), and the reaction temperature on the particle size and its distribution are investigated. With careful control of the synthesis condition, microspheres can be obtained with a particle size distribution of 1.09 (Dw/Dn). The average particle size of poly(ε-caprolactone) microspheres decreased with the increase in the molecular weight of poly(dodecyl acrylate) and increased with the increase in the relative content of 1,4-dioxane. The uniformity of microspheres decreased with the increase in the polymerization temperature.

Keywords

• dispersion polymerization
• poly(dodecyl acrylate)
• poly(ε-caprolactone) microspheres