A clean and efficient route for extraction of vanadium from vanadium slag by electro-oxidation combined with ultrasound cavitation

Abstract

Extracting vanadium (V) from vanadium slag (VS) by the traditional roasting-leaching process has disadvantages of high energy consumption and high poisonous gases emission. In this work, a green and efficient route was developed to extract V from VS without roasting by electro-oxidation combined with ultrasound cavitation (EOUC) intensification in sulfuric acid solution. The leaching parameters (e.g., leaching temperature, sulfuric acid concentration, anodic current density, ultrasound power, liquid to solid ratio, leaching time and particle size) were optimized. The leaching mechanism was explored by comparing the leaching behavior and mineralogical evolution of the direct sulfuric acidic leaching (DSL), electro-oxidation-assisted sulfuric acidic leaching (EOSL), ultrasound cavitation-assisted sulfuric acidic leaching (UCSL) and EOUC methods. The results show that introducing electric field strengthens the ultrasound cavitation effect on slag particles in sulfuric acid solution. Under the optimum parameter of EOUC method, the leaching rate of V from VS is as high as 94.64 %. Using EOUC method can open the silicate-wrapped structure of the spinel, increase pore volume of VS from 0.00127 cm3 g−1 to 0.01124 cm3 g−1, decrease slag particle size from 26.8 μm to 16.4 μm and improve specific surface area from 0.508 m2 g−1 to 10.855 m2 g−1, which significantly accelerate V leaching process. The exposed spinel was oxidized by both electrochemical route and chemical route, forming a mixture of V3+ ion and VO2+ ion after leaching.

Keywords

• Vanadium slag
• Electro-oxidation
• Ultrasound cavitation
• Vanadium leaching
• Mineralogy