Investigation on the properties of totally chlorine free bleached soda - oxygen pulp from old corrugated container

Abstract

Soda - oxygen pulping of old corrugated container to produce totally chlorine free bleached pulp was investigated. In order to reach the optimum delignification condition; four levels of sodium hydroxide (9, 11, 13, and 15 %), three cooking times (90, 120, and 150 minutes) and two cooking temperatures (120, and 150 ºC) at 6 bar oxygen pressure were studied. Yield and kappa number of pulps were measured. Results showed that the pulp obtained applying 9% sodium hydroxide, 150 minute delignification time and 150 ºC delignification temperature which produced the pulp with the yield and kappa number of 72.44% and 24.72 respectively was suitable for further bleaching. Strength of selected pulp including burst strength, tensile strength, and tear strength indices were measured as 2.27 kPa.m2/g, 29.19 Nm/g and 10.24 mN.m2/g respectively. The pulp was bleached applying 3% H2O2 and 2% NaOH to reach the final brightness of 57.97% ISO.

Keywords

• Soda/oxygen
• old corrugated container (OCC)
• delignification
• totally chlorine free
• ftrength properties