Mortars with Polypropylene Fibers Modified with Tannic Acid to Increase Their Adhesion to Cement Matrices

Abstract

The presented research’s main objective was to evaluate the possibility of improving the adhesion between polypropylene fibers and mineral matrices in cementitious composites by modifying the fibers’ surface with tannic acid (TA). This modifier was previously used for polyethylene fibers only. Cement mortar containing modified polypropylene fibers and mortar containing unmodified fibers were tested. The physical and mechanical properties (apparent density, compressive strength, flexural strength and modulus of elasticity) were determined, and the fibers’ morphology after the specimens’ destruction was observed. No adverse effect of the modification was found. The elastic modulus was 6% lower after 28 days, enabling the formation of a less stiff composite material. The integrity of the specimens after mechanical damage was improved, confirming the increased adhesion between the polypropylene fibers and the hardened cement paste. The results of the introductory tests are promising; however, further research is needed in the field.

Keywords

• adhesion
• cementitious composite
• fiber-reinforced concrete
• modification
• polypropylene fibers
• tannic acid