Response of a DIN 18MnCrSiMo6-4 Continuous Cooling Bainitic Steel to Plasma Nitriding with a Nitrogen Rich Gas Composition

Abstract

Abstract The use of continuous cooling bainitic steels can provide a more energy efficient manufacturing route. However, for their use in mechanical components like gears, it is necessary to improve their surface properties without impacting the core properties to guarantee reliable mechanical performance. The effect of temperature and time on the plasma nitriding response of a DIN 18MnCrSiMo6-4 steel was investigated. The plasma nitriding was performed for 3, 6 and 9 hours, at 400, 450, 500 and 550 °C, using a gas mixture composed of 76 vol.% nitrogen and 24 vol.% hydrogen. Samples were characterized before and after plasma nitriding concerning the microstructure, hardness and microhardness, fracture toughness, phase composition and residual stress states. Based on the results presented, layer growth constants (k) for different temperatures was determined. Moreover, it could be found that 500 °C gave the best results investigated here, as higher temperature took to core and surface hardness decrease. The nitrided samples with thicker compound layers presented a fracture behavior dominated by the formation of Palmqvist cracks. X-ray phase analysis indicated the formation of biphasic compound layer on the surface of all nitrided samples. The diffusion zone presented compressive residual stresses with highest values near the surface.

Keywords

• DIN 18MnCrSiMo6-4 Steel
• Plasma Nitriding
• Layer Growth Constant
• Fracture Toughness
• Residual Stress Analysis