New Insights into Flexible Transparent Conductive Silver Nanowires Films

Abstract

Flexible transparent conductive films (FTCFs) composed of silver nanowires (AgNWs) have become an important research direction because of their potential in flexible electronic devices. The optoelectronic properties of FTCFs composed of AgNWs of different lengths were evaluated in this study. AgNWs, with an average diameter of about 25 nm and length of 15.49−3.92 μm were obtained by a sonication-induced scission process. AgNW-FTCFs were prepared on polyethylene terephthalate substrates using a Meyer bar and then dried in the ambient environment. The sheet resistance, non-uniformity factor of the sheet resistance, the root mean square roughness, and haze of the FTCFs increased as the length of AgNWs decreased. The transmittance of the films increased slightly as the length of AgNWs increased. AgNWs with a length of 15.49 μm provided an AgNW-FTCF with excellent properties including haze of 0.95%, transmittance of 93.42%, and sheet resistance of 80.15 Ω∙sq−1, without any additional post-treatment of the film. This work investigating the dependence of the optoelectronic properties of AgNW-FTCFs on AgNW length provides design guidelines for development of AgNW-FTCFs.

Keywords

• silver nanowire
• flexible transparent conductive film
• sonication-induced scission
• haze