Preparación de un nuevo material híbrido orgánico/inorgánico mediante la intercalación de colina en bronce de molibdeno

Abstract

Intercalation of a organic compound, 2-hydroxyl etil trimetil ammonium, in the layered host molybdenum bronzes was achieved. Full characterization of solids was performed using chemical analysis, X-ray diffaction, thermal analysis and IR spectroscopy. Using fresh sodium hydrated layered molybdenum bronce yields a monofasic layered solid. The hybrid organic-inorganic compound exhibs a high lamellar order, which is stable at temperatura below 550 K, then collapsing by combustion of organic component. All features show that blue molybdenum bronzes will be a good host for intercalation.<br><br>Se aborda la intercalación de un compuesto orgánico, 2-hidroxil etil trimetil amonio (Colina), entre las láminas de bronce azul de molibdeno. El sólido obtenido se caracteriza mediante análisis químico (AQ), difracción de rayos-X (XRD), análisis térmico (DTA y TG) y espectroscopia infrarroja (FT-IR). La utilización de un bronce sódico de molibdeno recién preparado facilita la incorporación de la molécula orgánica, dando lugar a la formación de una única fase laminar. El material híbrido muestra un alto ordenamiento laminar, estable a temperaturas inferiores a los 550 K, que se descompone por combustión del componente orgánico. Los resultado obtenidos indican que el bronce azul de molibdeno puede ser un buen candidato para la obtención de compuestos de intercalación.

Keywords

• Molybdenum bronze
• hybrid organic-inorganic
• intercalation
• Bronce de Molibdeno
• Híbrido orgánico-inorgánico
• intercalación