Synthesis and Characterization of SiO₂/TiO₂ as Photocatalyst on Methylene Blue Degradation

Abstract

The paper presents a modification of titanium dioxide with fumed silica. The SiO2/TiO2 photocatalysts were obtained by the sol-gel method and then were calcined under an argon atmosphere. Various SiO2 weights (2–17.2 wt.%) were used in the materials’ preparation stage. The obtained samples were characterized using advanced analytical methods, such as FT-IR/DRS infrared spectroscopy, X-ray diffraction, SEM scanning electron microscopy, and UV-Vis/DRS spectroscopy. The BET specific surface area and zeta potential of samples were also measured. Based on the obtained results, it was observed that the modification of titanium dioxide with SiO2 effectively inhibited the increase in crystallite size of anatase and brookite during calcination and the decrease in specific surface area values. Moreover, the presence of SiO2 in the nanomaterials contributed to the increase in the size of specific surface area and the change in band gap energy values. The photocatalytic activity was determined based on the decomposition of methylene blue under UV irradiation. Thermal modification in an inert gas atmosphere significantly increased the dye removal rate. It should be noted that all the obtained SiO2/TiO2 photocatalysts showed higher activity compared to the starting TiO2. It was also found that the photocatalytic activity increased along with the increase in SiO2 content in the sample (up to 14.3 wt.% of SiO2). The highest activity was recorded for SiO2(11.1%)/TiO2_400 and SiO2(14.3%)/TiO2_400 samples.

Keywords

• photocatalysis
• titanium dioxide
• fumed silica
• methylene blue decomposition