Boletín de la Sociedad Española de Cerámica y Vidrio (Aug 2000)
Influencia del contenido metálico sobre las constantes ópticas de laminas delgadas amorfas de composición As<sub>33</sub>S<sub>67</sub> fotodopadas con Ag
Abstract
Agx(As0.33S0.67)100-x amorphous chalcogenide thin films have been prepared by the process of photodissolution or photodoping, reaching silver concentrations of up to 16.5 at. %. The optical constants of the photodoped thin-film samples have been calculated from the envelopes of the transmission spectra, taken at normal incidence. The dispersion of the refractive index was analysed on the basis of the single-oscillator model proposed by Wemple and DiDomenico. This model allows obtaining structural information of the silver-photodoped layers from optical data. The optical absorption edge is described using the non-direct transition model suggested by Tauc, and a clear decrease of the optical gap of the photodoped product, with the silver content, has been found.Se han preparado láminas delgadas amorfas calcogenuras de composición Agx(As0.33S0.67)100-x, mediante el fenómeno fotoinducido conocido como fotodisolución o fotodopaje, alcanzándose concentraciones de Ag en las muestras de hasta un 16.5 % at. Las constantes ópticas de las láminas fotodopadas, se han determinado haciendo uso de un método de caracterización basado en las envolventes de los espectros de transmisión óptica obtenidos en incidencia normal. El análisis de la dispersión del índice de refracción se ha realizado siguiendo el modelo propuesto por Wemple-DiDomenico, basado en la aproximación del oscilador armónico simple. Este modelo ha permitido obtener información estructural de las láminas fotodopadas, a partir de los resultados ópticos. El borde de absorción óptica de las láminas fotodopadas se ha analizado sobre la base del modelo de transición no directa propuesto por Tauc, encontrando una disminución del gap óptico del producto fotodopado, con el contenido de plata.