Design of Functional Polymer Systems to Optimize the Filler Retention in Obtaining Cellulosic Substrates with Improved Properties

Abstract

In the present work, the possibility of increasing the calcium carbonate (CaCO3) content in sheets of paper to optimize their properties was investigated. A new class of polymeric additives for papermaking is proposed as well as a method for their use in paper sheet containing the CaCO3 precipitated addition. Calcium carbonate precipitated (PCC) and fibers cellulose were adjusted with a cationic polyacrylamide flocculating agent (polydiallyldimethylammonium chloride (plyDADMAC) or cationic polyacrylamide (cPAM)). PCC was obtained in the laboratory by a double-exchange reaction between calcium chloride (CaCl2) and sodium carbonate (Na2CO3) suspension. After testing, the dosage of PCC was established at 35%. To improve the systems of additives studied, the materials obtained were characterized and their optical and mechanical properties were analysed. The PCC had a positive influence over all of the paper samples, but in the case of use of cPAM and polyDADMAC polymers the paper obtained had superior properties compared to the paper obtained without additives. Also, the samples obtained in the presence of cationic polyacrylamide exhibit superior properties to those obtained in the presence of polyDADMAC.

Keywords

• calcium carbonate precipitated (PCC)
• cationic polyacrylamide (cPAM)
• cellulosic substrates
• filler
• mechanical and optical properties
• polyDADMAC