Tribological Properties of Ti6Al4V Titanium Textured Surfaces Created by Laser: Effect of Dimple Density

Abstract

The loss of energy due to friction is one of the major problems industries are facing nowadays. Friction and wear between sliding components reduce the mechanical efficiency of machines and have a negative impact on the environment. In recent years, surface texturing has shown tremendous ability to reduce friction and wear. Micro-features generated on surfaces act as a secondary reservoir for lubricants and wear debris receptacles to further reduce abrasion. In addition, surface texturing boosts hydrodynamic pressure, which increases the elasto-hydrodynamic lubrication regime of the Stribeck curve, reducing friction and wear. Amongst all different techniques to texture surfaces, laser texturing is the most popular due to its advantages such as high accuracy, good consistency and celerity as compared to other techniques. This study investigated the effect of laser texturing on the tribological properties of Ti6Al4V in contact with a ceramic ball. The effect of varying the dimple density on friction and wear was studied using a ball-on-flat reciprocating tribometer under lubricated conditions. Results show that friction and wear were reduced for all the textured samples as compared to an untextured sample, with important friction and wear reductions for the samples with the highest dimple densities. For samples with intermediate dimple densities, the friction coefficient stayed low until the dimples wore out from the surface and then increased to a value similar to the friction coefficient of the untextured surface. The dimple wear-out time observed in these specimens was greatly influenced by the dimple density.

Keywords

• textured surfaces
• friction
• wear
• lubrication
• titanium