Optimized Tribological Performance of Nitrogen-Doped Diamond-like Carbon Films on NBR: Influence of Bias Voltage of DC Magnetron Sputtering

Abstract

In this research, nitrogen-doped diamond-like carbon (N-DLC) coatings were deposited on Nitrile Butadiene Rubber (NBR) substrates using direct current magnetron sputtering (DC-MS) under varying bias voltages. This study aimed to explore environmentally friendly, low-wear, and non-lubricating seal coatings to enhance the durability of rubber sealing products, which predominantly operate under dynamic sliding conditions. By reducing the coefficient of friction (CoF), the friction and wear on rubber products can be significantly minimized, extending their lifespan. This investigation thoroughly examined the microstructure, mechanical properties, and tribological behavior of the N-DLC films. Among the coatings, the one produced at a bias voltage of −50 V demonstrated superior hardness, elastic modulus, and the lowest CoF in comparison to those prepared with 0, −100, and −200 bias voltages. This optimal combination of properties resulted in an exceptionally low wear rate of 10−9 for the film deposited at −50 V, indicating its outstanding wear resistance.

Keywords

• NBR
• DLC films
• nitrogen-doped
• bias voltage
• tribological properties