Contemporary Clinical Dentistry (Jan 2017)
Effect of water storage on the flexural strength of heat-cured denture base resin reinforced with stick (s) glass fibers
Abstract
Background: Flexural strength (FS) of denture base resins (DBRs) had been improved by reinforcing it with different glass fibers. However, a limited data are available on the effect of glass fiber reinforcement with conventional heat-cured resin after prolonged water storage. Aims and Objectives: This study aimed to evaluate the reinforcing effect of novel S-glass and nylon fibers on the FS of acrylic DBRs. It also aimed to evaluate the effect of glass fiber reinforcement on the FS of acrylic DBRs after a prolonged storage in water. Materials and Methods: One hundred and sixty identical specimens were fabricated in specially designed molds according to the manufacturer's instructions. The three experimental groups were prepared consisting of conventional (unreinforced) acrylic resin, novel S-glass fiber-reinforced and nylon fiber-reinforced acrylic resin. The specimens were fabricated in a standardized fashion for each experimental group. Each group was further subdivided into two groups on the basis of storage conditions (dry and wet). FS was tested using a three-point universal testing machine at a crosshead speed of 5 mm/min. Glass fiber-reinforced group was further tested after prolonged storage in distilled water. Entered data were statistically analyzed with one-way ANOVA and least significant difference post hoc test. Results: In this study, statistically significant differences were noted in the FS of all the groups. S-glass fiber-reinforced group had highest FS compared to the other two groups (P < 0.001). Nylon fiber-reinforced group had lowest FS. All the groups stored in distilled water revealed a decrease in strength compared to those stored in dry atmosphere. Among wet specimens, those stored for 3 weeks had a significantly higher FS than those stored at one and 2 weeks (P < 0.01). Conclusion: Within the limitations of this investigation, the FS of heat-cured acrylic DBR was improved after reinforcement with glass fibers. It can be recommended to strengthen distal extension partial and complete denture bases. Nylon fibers may not be desirable for strengthening acrylic denture bases.
Keywords