Determinación experimental de la sección isotermal de 1300º C del Sistema CaO – Al₂O₃ – CoO

Abstract

The subsolidus of the system CaO-Al2O3-CoO has been studied. Was established the existence of nine compatibility triangles. It had been found a phase Ca3Al4CoO10, isoestructural to Ca3MgAl4O10. Solid solutions of CaO, CoO and CoAl2O4 were determinated. Color variation on diferent samples was observed as function of the phase diagram region. When Co was substituted for other bivalents cations (Sr, a, n, Ni, Cu, Cd, Sn and Pb), were not found new phases. This study depicts the most outstanding results concerning the alternate materials research line. The importance focused on the stability of the new compound into the matrix of other materials from some technological processes such as the cement one, into which industrial wastes can be incorporated as alternate raw materials and fuels.Se ha estudiado el subsolidus del sistema CaO-Al2O3-CoO estableciendo la existencia de nueve triángulos de compatibilidad en estado sólido. Se ha encontrado una fase de fórmula Ca3CoAl4O10 isoestructural a Ca3MgAl4O10. Se ha establecido la existencia de soluciones sólidas de Co en CaO, de Ca en CoO y en CoAl2O4. Se ha observado la formación de fases con diversos colores en función de la zona del diagrama. Al sustituir Co por otros cationes bivalentes (Sr, Ba, Mn, Ni, Cu, Cd, Sn y Pb) no se encontraron nuevas fases. Este estudio presenta los resultados más relevantes en relación con la línea de investigación del uso de materiales alternos. La relevancia se enfoca en mantener la estabilidad de un nuevo compuesto en la matriz de algún proceso tecnológico, como por ejemplo el proceso del cemento, en el cual pueden ser incorporados desechos industriales como materias primas y combustibles alternos.

Keywords

• Phase diagrams
• alternate materiales
• new technologies
• diagramas de fase
• materiales alternos
• nuevas tecnologías