The Initial Assessment of the Possibility of Simulation Fire Standard Curve in the Electric Furnace with the Assessment of Chemical Composition Changes in Steel after Cooling Phase

Abstract

The article focuses on analyzing changes in the chemical composition of steel samples after the cooling phase. A few distinct types of samples made of St3S steel were heated in an electric resistance furnace for 1 h. The temperature in the following minutes of the furnace work was programmed to reflect the standard fire curve defined in the Eurocode in the best possible way. The box-type electric furnace was used. There were three series of samples, and each of them was cooled down in diverse ways: (a) in the water, (b) in the polymer cooling medium AQUA-QUENCH® 320, and (c) in the furnace. After that, the chemical composition of diverse types of samples with various kinds of cooling was checked. This task was realized using a laser elementary analysis microscope with the EA-300 head. The investigation allowed the authors to draw the following conclusions: the electric furnace may be used to simulate an increase in temperature with fire duration according to standard fire curve only in the phase of fully developed fire situation; the EA-300 head for laser elementary analysis allows checking of the chemical composition of investigated elements very quickly (in a few seconds).

Keywords

• chemical composition
• steel samples
• fire exposition
• electric furnace
• standard fire curve
• LIBS