Development of resin-based bioactive endodontic cements with glycerol salicylate and calcium silicate

Abstract

Introduction: The combination of sol-gel derived calcium silicate particles and glycerol salicylate resins may enhance the pyhisico-chemical properties contribute to the understanding of the interaction between these materials. This study aims to evaluate the physical-chemical properties of resin-based bioactive endodontic cements with glycerol salicylate resins and calcium silicate particles. Materials and methods: Calcium silicate was produced by the sol-gel route, while the resin was produced by mixing 60wt% glycerol salicylate, 30wt% methyl salicylate and 10wt% distilled water. Calcium silicate was added in three different concentrations, 50, 40 and 25% by weight. The cement was tested for setting time, flow, radiopacity and pH. Results: The 50:50 group shows the time of 15min8s while the 75:25 shows the time of 256min13s (p