Improved Wood-Bond Strengths Using Soy and Canola Flours with pMDI and PAE

Abstract

The surprising lack of literature on using the very common wood adhesive polymeric methylenediphenyl diisocyanate (pMDI) with protein adhesives may be because of perceived poor improvement of protein wet strength. Reacting pMDI with the flour (soy or canola) before adding water unexpectedly improves wood bonding compared to adding the pMDI to an aqueous protein slurry. Mixing the liquid pMDI with the oilseed flour produces a free-flowing powder with up to 50% of pMDI to flour by weight. The mixture slowly reacts since the isocyanate band in the infrared spectra remains for several days but diminishes with time. Adding pMDI increases the dry and wet strength of wood bonds using Automated Bonding Evaluation System (ABES) testing and levels off at about 50%. Similarly, adding the polyamidoamine-epichlorohydrin (PAE) cross-linker to the oilseed flour increases dry and wet bond strength, but the effect levels off at about 20% of PAE. However, the combination of these two cross-linkers added to the flours results in greater dry and wet shear strength than either one alone. In addition to tests using ABES (ASTM D 7998), the increase in strengths is also observed—but with a diminished effect—in bonding plywood using the interior plywood strength test ASTM D 906.

Keywords

• soy flour
• canola flour
• wood adhesive
• shear strength
• water resistance
• pMDI