Highly conformal and high-ionic conductivity thin-film electrolyte for 3D-structured micro batteries: Characterization of LiPON film deposited by MOCVD method

Abstract

This paper reports a lithium phosphorus oxynitride (LiPON) thin-film electrolyte deposited using a metalorganic-chemical vapor deposition (MOCVD) method for 3D-structured micro batteries. It is shown that the MOCVD-LiPON film has both highly-conformal step coverage on a patterned substrate with line/space=2μm/2μm and aspect ratio=1 (51±3 nm) and high-ionic conductivity for very thin films deposited at 4.7 nm/min (5.9×10-6 S/cm for 190 nm and 5.3×10-6 S/cm for 95 nm). Detailed material characterization attributes the enhancement in ionic conductivity to a decrease in nanocrystallite size and improvement in chemical-composition uniformity in the film. In addition, electrochemical characterization of an all-solid-state thin-film battery fabricated with the 190 nm-thick LiPON film (Si substrate/Ti/Pt/LiCoO2/LiPON/a-Si:H/Cu) demonstrates that the LiPON film can successfully act as the electrolyte for lithium-ion batteries. Therefore, the MOCVD-LiPON film is a promising candidate material to realize 3D-structured micro batteries in the near future.