Microtextural aspects of the chemical corrosion in Pierce-Smith converters (PSC)

Abstract

Microtextural studies are often the basis for projects proposing improvements in the quality of refractory coatings that come into contact with aggressive molten material. The material used for this analysis either comes from laboratory-level corrosion tests or from furnace walls and linings that have come to the end of their working cycle. This article aims to evaluate the reach of the chemical wear mechanism with a microtextural study of samples that have been in industrial use. However, other wear mechanisms should be taken into consideration; acting in parallel they can be even more important quantitatively than the chemical wear itself which results from the microtextural analysis of the samples.<br><br>Los estudios microestructurales han estado frecuentemente en la base de proyectos orientados a la mejora en la calidad de los revestimientos refractarios destinados a estar en contacto con metales fundidos. Los materiales empleados en este trabajo proceden de las paredes de hornos que están en la fase final de su vida útil. El trabajo intenta asociar el mecanismo de corrosión química existente con las modificaciones microestructurales encontradas en piezas utilizadas en planta. No obstante, debería considerarse que existen otros mecanismos de corrosión, que actuando en conjunción con los arriba descritos podrían ser más relevantes desde el punto de vista cuantitativo que la corrosión química detectada en los análisis micorestructurales de las muestras.

Keywords

• Pierce-Smith Converter
• Wear mechanisms
• Refractory
• Microstructure
• Convertidor Pierce-Smith
• mecanismos de corrosión
• refractarios
• microestructura