Boletín de la Sociedad Española de Cerámica y Vidrio (Jun 2000)
Tratamiento mecanoquímico de la ferrita MgFe<sub>2</sub>O<sub>4</sub>
Abstract
Powder of MgFe2O4, previously prepared by solid state reaction, was mechanochemically treated in a centrifugal ball mill in air atmosphere. Different milling conditions has been employed varying ball/powder mass ratio. After low milling time a strong reduction on crystallite size has been detected while the strain lattice increase slowly. The presence of α-Fe2O3 was also observed at different milling time, depending on milling conditions, by means of X-Ray diffraction experiments. Magnetic transition temperatures were evaluated using a thermogravimetric analyser, equipped with a small permanent magnet. An attempt of dependence of magnetic properties with crystallite size has been established.La ferrita MgFe2O4, en forma de polvo y previamente preparada por reacción en estado sólido, se ha sometido a un proceso de molienda mecánica en atmósfera de aire usando un molino centrífugo. Se emplearon diferentes condiciones de molienda variando la relación de peso bolas/ferrita. La variación del tamaño de dominio cristalino o de cristalita y lamicrodeformaciones de red a escala de celda unidad se evaluaron mediante difracción de rayos-X de polvo. Para bajos tiempos de molienda se observó una acusada disminución del tamaño de dominio cristalino, mientras que las microdeformaciones de la red experimentaron un ligero aumento. Así mismo, a partir de determinados tiempos de molienda, se detectó la presencia de α-Fe2O3. Las temperaturas de transición magnética fueron evaluadas a partir de un analizador termogravimétrico equipado con un pequeño imán permanente y se estableció un correlación entre la temperatura de Curie y el tamaño de dominio cristalino.