The Tuning Capability of CuO and Na₂CO₃ Dopant on Physical Properties for Laser Sealing Using Fiber Types of Sealant

Abstract

PbO-SiO2-Al2O3-B2O3 (PSAB)-based glasses were prepared in order to determine the feasibility for laser sealing in the form of fiber. To reach a high quality of laser sealing, the tuning capability of CuO and Na2CO3 dopant concentration was examined on thermal, thermo-mechanical, and optical properties of glasses. The difference of thermal expansion coefficient was reduced with codoping of 1 wt% CuO-2 wt% Na2CO3 into the PSAB glass system, and it amounted to 0.34 × 10−6/K. The codoped PSAB glass system reached 100% absorption at 810 nm, which corresponds to the wavelength of laser. The glass fiber with a diameter of 180 μm was successfully pulled from the codoped PSAB glass system. The fluorine-doped tin oxide (FTO) glass substrate using the glass fiber was successfully sealed. It presented a crack-free sealed surface with a sealing strength of about 41 MPa. These results indicate that the PSAB-based glass system in the form of fiber is proved as a laser sealing material in packaging systems.

Keywords

• lead silicate glass
• glass transition temperature
• coefficient of thermal expansion
• glass fiber
• laser sealing