Improving the ablation resistance of epoxy modified organosilicon resin synergistic modified with B2O3 and ZrSi2

Abstract

The boron oxide and zirconium silicide synergistic modified epoxy modified organosilicon resin composites were prepared and the ablation resistance properties of the composites were analyzed. With the synergistic effect of boron oxide and zirconium silicide, the properties, such as: the residue yield, hardness, tensile strength and ablation resistance (oxyacetylene ablation and static muffle furnace ablation) of the samples are markedly enhanced. The oxyacetylene linear ablation rate of the modified composite was observed to the minimum (0.04 mm s ^−1 ), when the contents of resin, boron oxide and zirconium silicide are 100 g, 50 g, and 150 g, respectively. The skeleton-like compact structure formed in the surface of composites after oxyacetylene ablation, which results in the best ablation resistance.

Keywords

• ablation resistance
• epoxy modified organosilicon resin
• synnergistic modified
• boron oxide
• zirconium silicide