Investigation of the Machined Surface Integrity of WC-High-Entropy Alloy Cemented Carbide

Abstract

A fine-grained WC-15wt%Al0.5CoCrFeNi cemented carbide was prepared through a vacuum and gas pressure sintering. For achieving high surface integrity, diamond wheel grinding serves as the primary molding process for the machining of WC cemented carbide. To reveal the influence of grinding on the surface integrity of fine-grained WC-HEA cemented carbide, studies were conducted on grinding force, surface microstructure, surface roughness, residual stress, microhardness, and bending strength. The morphological analysis of the ground surface indicated a transition in the material removal mechanism of WC-HEA cemented carbide from ductile removal to brittle removal, with brittle removal becoming predominant as the depth of grinding increases. With the increasing depth of grinding, the grinding force increases, and the grinding force increases while the surface roughness decreases. Correspondingly, there is an improvement in both hardness and bending strength. Additionally, grinding induces high residual compressive stress on the surface, with a maximum compressive stress of 1795 MPa. The bending strength of the material is found to be dependent on the residual stress.

Keywords

• WC-HEA cemented carbide
• grinding
• surface integrity