Transient Liquid Phase Behavior of Sn-Coated Cu Particles and Chip Bonding using Paste Containing the Particles

Abstract

Sn-coated Cu particles were prepared as a filler material for transient liquid phase (TLP) bonding. The thickness of Sn coating was controlled by controlling the number of plating cycles. The Sn-coated Cu particles best suited for TLP bonding were fabricated by Sn plating thrice, and the particles showed a pronounced endothermic peak at 232°C. The heating of the particles for just 10 s at 250°C destroyed the initial core-shell structure and encouraged the formation of Cu-Sn intermetallic compounds. Further, die bonding was also successfully performed at 250°C under a slight bonding pressure of around 0.1 MPa using a paste containing the particles. The bonding time of 30 s facilitated the bonding of Sn-coated Cu particles to the Au surface and also increased the probability of network formation between particles.

Keywords

• Sn-coated Cu
• immersion plating
• chip bonding
• transient liquid phase (TLP) sintering
• intermetallic compounds (IMC)