Materials (May 2014)

An Optimal Cure Process to Minimize Residual Void and Optical Birefringence for a LED Silicone Encapsulant

  • Min-Jae Song,
  • Kwon-Hee Kim,
  • Gil-Sang Yoon,
  • Hyung-Pil Park,
  • Heung-Kyu Kim

DOI
https://doi.org/10.3390/ma7064088
Journal volume & issue
Vol. 7, no. 6
pp. 4088 – 4104

Abstract

Read online

Silicone resin has recently attracted great attention as a high-power Light Emitting Diode (LED) encapsulant material due to its good thermal stability and optical properties. In general, the abrupt curing reaction of the silicone resin for the LED encapsulant during the curing process induces reduction in the mechanical and optical properties of the LED product due to the generation of residual void and moisture, birefringence, and residual stress in the final formation. In order to prevent such an abrupt curing reaction, the reduction of residual void and birefringence of the silicone resin was observed through experimentation by introducing the multi-step cure processes, while the residual stress was calculated by conducting finite element analysis that coupled the heat of cure reaction and cure shrinkage. The results of experiment and analysis showed that it was during the three-step curing process that the residual void, birefringence, and residual stress reduced the most in similar tendency. Through such experimentation and finite element analysis, the study was able to confirm that the optimization of the LED encapsulant packaging process was possible.

Keywords