Boletín de la Sociedad Española de Cerámica y Vidrio (Feb 1999)
Cristalización de cordierita a partir de geles y vidrios estequiométricos. Estudio comparativo
Abstract
The influence of precursor, gel and glass, on cordierite crystallization has been studied in the system MgO-Al2O3-SiO2. Also is compared the effect of superficial or bulk-crystallization, in powder or monolithic glass, on the sequence of crystallized phases and their microstructural evolution. After the same temperature treatment, the crystalline phases were analysed by X-ray Diffraction (DRX) and Field Emission Scanning Electron Microscopy (FESEM), where it seams clear that the final morphology of hexagonal cordierite agrees hexagonal prisms with 5-10 μm of external radius and variable length. Only the glass-derived cordierite has shown secondary phases, as mullite and enstatite, what were stable for all studied temperatures.<br><br>Se ha estudiado la influencia del precursor, gel y vidrio, sobre la cristalización de la cordierita estequiométrica dentro del sistema ternario MgO-Al2O3-SiO2. Así mismo se compara el efecto, en el caso de muestras vítreas en polvo prensado o monolito, del tipo de cristalización (mayoritariamente superficial o en volumen), en la secuencia de fases y la evolución microestructural. Se han analizado, tras un mismo tratamiento térmico para todas las muestras, las fases cristalizadas por difracción de polvo de rayos X, así como su microestructura por microscopia electrónica de barrido (M.E.B.), donde parece claro que la morfología final de la cordierita hexagonal, tras pasar por varios estadios, es en forma de prismas hexagonales de diámetro entre 5 y 10 μm y longitud variable. La cordierita derivada del gel no presentó fases secundarias estables en los tratamientos térmicos aplicados, no así las derivadas del vidrio, donde la enstatita (MgO-SiO2) y la mullita (3Al2O3-2SiO2) aparecieron en pequeñas cantidades durante casi todo el intervalo de temperaturas empleadas.