Heliyon (Jul 2024)

Electrical transport and dielectric relaxation mechanism in Zn0.5Cd0.5Fe2O4 spinel ferrite: A temperature- and frequency-dependent complex impedance study

  • Raheel Mumtaz,
  • Waqar Hussain Shah,
  • Yousaf Iqbal,
  • Hayat Ullah,
  • Ghulam Asghar,
  • Mubushar Hussain,
  • Mostafa R. Abukhadra,
  • Ahmed M. El-Sherbeeny

Journal volume & issue
Vol. 10, no. 14
p. e34155

Abstract

Read online

In the present study, the frequency-dependent dielectric relaxation and electrical conduction mechanisms in sol-gel-derived Zn0.5Cd0.5Fe2O4 (ZCFO) spinel ferrite were studied in the temperature range of 343–438 K. The formation of the ZCFO spinel ferrite phase with space group Fd3m was confirmed by X-ray diffraction analysis. The dielectric relaxation and electrical conduction mechanisms were studied using complex impedance spectroscopy (CIS). In the Nyquist plots, depressed semicircles were fitted with an equivalent circuit model with configuration (RGBQGB) (RGQG), signifying the contributions from grain boundaries and grains to the charge transport mechanism in the sample. The frequency-dependent AC conductivity was found to follow Jonscher's power law, and the frequency exponent term depicted the overlapping large polaron hopping (OLPH) model as the dominant transport mechanism. The activation energies for conductivity, electric modulus and impedance were calculated to identify the nature of the charge carriers governing the relaxation and conduction mechanisms in the prepared sample. Complex modulus studies confirmed the non-Debye type of dielectric relaxation, whereas tangent loss and dielectric constant analyses confirmed the thermally activated hopping mechanism of charge carriers in Zn0.5Cd0.5Fe2O4 spinel ferrite.

Keywords