Boletín de la Sociedad Española de Cerámica y Vidrio (Aug 2000)
Degradación hidrolítica de recubrimientos polisiloxánicos de fibras de vidrio
Abstract
Aqueous solutions of three silanes: 3-aminopropyltriethoxysilane (APES), 3-aminopropylmethyldiethoxysilane (APDES), and 3-aminopropyldimethylethoxysilane (APMES), were used to cover glass fibers. The pyrenesulfonyl chloride fluorescent moiety (PSC) was chemically attached to the silanized substrate via the sulfonamide formation when the sulfonyl group of the PSC reacts with the amino residues of the coatings. It was studied the silane layer hydrolytic degradation phenomenon (pH = 7) was studied as a function of: i) temperature, and ii) coating layer type. A hydrolysis reaction mechanism of the polysiloxane bonded onto the glass fibers has been proposed and, the enthalpy change of the process was obtained (3.5 kcal/ mol). In addition, it was observed that the greater the silane functionality the faster the hydrolytic degradation.<br><br>Se silanizaron fibras de vidrio mediante la utilización de disoluciones acuosas de tres silanos: 3-aminopropiltrietoxisilano (APES), 3-aminopropilmetildietoxisilano (APDES) y 3-aminopropildimetiletoxisilano (APMES). Se injertó químicamente una molécula fluorescente (cloruro de pirenosulfonilo, PSC) mediante la formación de una sulfonamida por reacción del grupo sulfonilo del PSC con los grupos amino de los recubrimientos. Se estudió el fenómeno de degradación hidrolítica del recubrimiento silano a pH = 7 en función de: i) la temperatura y ii) el tipo de recubrimiento. Se ha propuesto un mecanismo para la reacción de hidrólisis del polisiloxano enlazado a las fibras de vidrio y se ha obtenido la entalpía del proceso, cuyo valor fue de 3.5 kcal/mol. También se ha observado que a medida que la funcionalidad del silano aumenta, la degradación hidrolítica es más rápida.