Preparation of Oxygen Reduction Catalyst Electrodes by Electrochemical Acidification and Synergistic Electrodeposition

Abstract

A proton exchange membrane fuel cell (PEMFC) is an efficient and environmentally friendly power production technology that uses hydrogen energy. The cathodic oxygen reduction electrode is a critical component in the development of PEMFC. Most techniques deposit catalyst nanoparticles in areas that are inaccessible for catalytic processes, reducing platinum utilization. The substrate used in this study was carbon paper (CP) with a self-supporting structure. First, electrochemical acidification technology was employed to modify the CP’s surface, followed by nanoparticle manufacturing and fixation on the CP in a single step by electrodeposition. The Pt/C0.5V2.24CP catalyst electrode demonstrated high-quality activity in the oxygen reduction reaction (ORR), with a homogeneous particle dispersion and particle size of around 50 nm. The mass activity and electrochemical active surface area (ECSA) of the Pt/C0.5V2.24CP catalyst electrode were 1.74 and 3.98 times higher than those of the Pt/C/CP-1 electrodes made with commercial catalysts, respectively. After 5000 cycles of accelerated durability testing (ADT), the mass activity and ECSA were 1.28 times and 6.16 times more than Pt/C/CP-1. This paper successfully proved the viability of electrodepositing Pt nanoparticles on CP following acidification, and that the electrochemical acidification methods have a positive influence on improving electrode ORR activity.

Keywords

• fuel cell
• oxygen reduction reaction
• electrodeposition
• catalyst electrode