Transition-Layer Implantation for Improving Magnetoelectric Response in Co-fired Laminated Composite

Abstract

Magnetoelectric (ME) laminated composites with strong ME coupling are becoming increasingly prevalent in the electron device field. In this paper, an enhancement of the ME coupling effect via transition-layer implantation for co-fired lead-free laminated composite (80Bi0.5Na0.5TiO3-20Bi0.5K0.5TiO3)/(Ni0.8Zn0.2)Fe2O4 (BNKT/NZFO) was demonstrated. A transition layer composed of particulate ME composite 0.5BNKT-0.5NZFO was introduced between the BNKT piezoelectric layer and the NZFO magnetostrictive layer, effectively connecting the two-phase interface and strengthening interface stress transfer. In particular, an optimal ME voltage coefficients (αME) of 144 mV/(cm·Oe) at 1 kHz and 1.05 V/(cm·Oe) at the resonant frequency in the composite was achieved, with a layer thickness ratio (BNKT:0.5BNKT-0.5NZFO:NZFO) of 3:1:6. The static elastic model was used to determine strong interface coupling. A large magnetodielectric (MD) response of 3.95% was found under a magnetic field excitation of 4 kOe. These results demonstrate that transition-layer implantation provides a new path to enhance the ME response in co-fired laminated composite, which can play an important role in developing magnetic field-tuned electronic devices.

Keywords

• magnetoelectric coupling
• laminated composite
• transition layer
• co-firing